標題: Titlebook: Consequences of Combinatorial Studies of Positive Electrodes for Li-ion Batteries; Eric McCalla Book 2014 Springer International Publishin [打印本頁] 作者: CT951 時間: 2025-3-21 18:52
書目名稱Consequences of Combinatorial Studies of Positive Electrodes for Li-ion Batteries影響因子(影響力)
書目名稱Consequences of Combinatorial Studies of Positive Electrodes for Li-ion Batteries影響因子(影響力)學科排名
書目名稱Consequences of Combinatorial Studies of Positive Electrodes for Li-ion Batteries網(wǎng)絡(luò)公開度
書目名稱Consequences of Combinatorial Studies of Positive Electrodes for Li-ion Batteries網(wǎng)絡(luò)公開度學科排名
書目名稱Consequences of Combinatorial Studies of Positive Electrodes for Li-ion Batteries被引頻次
書目名稱Consequences of Combinatorial Studies of Positive Electrodes for Li-ion Batteries被引頻次學科排名
書目名稱Consequences of Combinatorial Studies of Positive Electrodes for Li-ion Batteries年度引用
書目名稱Consequences of Combinatorial Studies of Positive Electrodes for Li-ion Batteries年度引用學科排名
書目名稱Consequences of Combinatorial Studies of Positive Electrodes for Li-ion Batteries讀者反饋
書目名稱Consequences of Combinatorial Studies of Positive Electrodes for Li-ion Batteries讀者反饋學科排名
作者: clarify 時間: 2025-3-21 20:31 作者: 大廳 時間: 2025-3-22 01:03
Optimization of the Synthesis of Combinatorial Samples,the main source of lithium loss was the decomposition of lithium carbonate that failed to react with the nickel oxide structure. The fact that the formation of LiNiO. was hindered significantly in air was attributed to the presence of constituents in air other than oxygen and nitrogen, the likeliest作者: 交響樂 時間: 2025-3-22 08:32 作者: 他一致 時間: 2025-3-22 10:39
,Combinatorial Studies of the Spinel and Rocksalt Regions in the Li–Mn–Ni–O System, and when quenched or regular cooled in oxygen. All samples discussed here either contained one or two phases; and no evidence for nonequilibrium behaviour was seen. Two-phase fits in the coexistence regions were used to determine lattice parameters to allow the drawing of tie-lines. The lever rule 作者: IVORY 時間: 2025-3-22 15:31 作者: IVORY 時間: 2025-3-22 20:21 作者: 拋射物 時間: 2025-3-23 00:47 作者: ureter 時間: 2025-3-23 02:19
Materials Near the Layered Boundary,under various oxygen partial pressures and were related to features in the phase diagram determined previously. Materials made with 5?. excess lithium (at point B. in Fig.?.) were found to stay single phase even when the regular cooling rate of 5–10?°C/min was used. These single-phase layered materi作者: 飲料 時間: 2025-3-23 08:30
Conclusions and Future Works,nched from 800?°C. Some approximations were made to join the two faces since the Li-Co-Mn-O face was synthesized in air while the nickel containing samples were made in oxygen. Nonetheless, the two faces join quite well. The pyramid strongly suggests that both single-phase regions of importance for 作者: reperfusion 時間: 2025-3-23 13:36 作者: monochromatic 時間: 2025-3-23 14:18
Colin McEwan,Maria-Isabel Silvahout this section, the method used to make samples in the Li-Mn-Ni-O system will be described. The only variation needed to make samples in the Li-Co-Mn-O system is to replace the nickel starting solution with a cobalt solution (both were nitrates in these studies). This method, developed by Carey a作者: 一小塊 時間: 2025-3-23 18:51
Sarah Byrne,Anne Clarke,Robin Torrencethe main source of lithium loss was the decomposition of lithium carbonate that failed to react with the nickel oxide structure. The fact that the formation of LiNiO. was hindered significantly in air was attributed to the presence of constituents in air other than oxygen and nitrogen, the likeliest作者: Physiatrist 時間: 2025-3-23 23:55
Axial Scattering from Thin Conesd that the layered region is a single composition line corresponding to cobalt being constrained to the 3+ oxidation state only. This composition line, joining LiCoO. to Li.MnO., was a solid solution over its entire length when samples were quenched from either 800 or 900?°C. Upon slow cooling, the 作者: Incumbent 時間: 2025-3-24 03:16
Sarah Anderson,Anthony H. Winefield and when quenched or regular cooled in oxygen. All samples discussed here either contained one or two phases; and no evidence for nonequilibrium behaviour was seen. Two-phase fits in the coexistence regions were used to determine lattice parameters to allow the drawing of tie-lines. The lever rule 作者: CONE 時間: 2025-3-24 08:45
Douglas C. Maynard,Daniel C. Feldmanow cooling they convert to structures containing at least some R and M phases. Though the thermodynamics of this are complex, a qualitative understanding can be achieved by considering the results of the Rietveld refinement. The R and M phases were collectively more ordered than the N and S phases (作者: neolith 時間: 2025-3-24 12:43
Sarah Anderson,Anthony H. Winefieldzed under various conditions via two different synthesis routes. The four-phase equilibrium was observed and transformations were found to be reversible, thereby confirming that two three-phase regions exist and transform during slow cooling. The primary importance of this work is a better understan作者: LUDE 時間: 2025-3-24 18:00 作者: 聰明 時間: 2025-3-24 21:30
Douglas C. Maynard,Daniel C. Feldmanunder various oxygen partial pressures and were related to features in the phase diagram determined previously. Materials made with 5?. excess lithium (at point B. in Fig.?.) were found to stay single phase even when the regular cooling rate of 5–10?°C/min was used. These single-phase layered materi作者: Costume 時間: 2025-3-25 02:21
David S. Pedulla,Katherine S. Newmannched from 800?°C. Some approximations were made to join the two faces since the Li-Co-Mn-O face was synthesized in air while the nickel containing samples were made in oxygen. Nonetheless, the two faces join quite well. The pyramid strongly suggests that both single-phase regions of importance for 作者: BANAL 時間: 2025-3-25 06:23 作者: Hyperlipidemia 時間: 2025-3-25 10:13 作者: Lipohypertrophy 時間: 2025-3-25 13:55 作者: 不能仁慈 時間: 2025-3-25 19:04
Springer Theseshttp://image.papertrans.cn/c/image/235724.jpg作者: 注意力集中 時間: 2025-3-25 22:18 作者: inhumane 時間: 2025-3-26 02:52
Book 2014to synthesis conditions used commercially.?The results?help resolve a number of points of confusion and contradiction in the literature.?Amongst other important findings, the compositions and synthesis conditions giving rise to layered-layered nano-composites are presented and electrochemical result作者: 拘留 時間: 2025-3-26 07:21 作者: confide 時間: 2025-3-26 11:24 作者: 不能仁慈 時間: 2025-3-26 16:11 作者: 自負的人 時間: 2025-3-26 17:07 作者: 拾落穗 時間: 2025-3-27 00:29 作者: Lucubrate 時間: 2025-3-27 03:10 作者: intricacy 時間: 2025-3-27 06:15
Materials Near the Layered Boundary, broadening only seen at high angle, consistent with the first sign of phase separation into layered–layered nano-composites. The dramatic loss in capacity seen in the sample made in 2?. oxygen at point A. can be attributed to nickel clustering on the lithium layer such that lithium islands form, ma作者: Lineage 時間: 2025-3-27 10:54
Conclusions and Future Works,ace. The spinel-layered co-existence region is also simpler in the Li–Co–Mn–O triangle with all tie-lines connecting to either the cobalt spinel, Co.O., or the manganese layered material, Li.MnO., while in the Li–Mn–Ni–O system there are 2 three-phase regions. The differences between the roles of co作者: ORE 時間: 2025-3-27 17:07
2190-5053 confusion and contradiction in the literature.?Amongst other important findings, the compositions and synthesis conditions giving rise to layered-layered nano-composites are presented and electrochemical result978-3-319-38317-0978-3-319-05849-8Series ISSN 2190-5053 Series E-ISSN 2190-5061 作者: adjacent 時間: 2025-3-27 21:31 作者: 出處 時間: 2025-3-28 01:24 作者: commensurate 時間: 2025-3-28 02:29
Sarah Byrne,Anne Clarke,Robin Torrenceefore result in lithium content very close to that seen in oxygen, the only difference being attributed to a slight increase in the rate of decomposition of lithium nickel oxide as seen in the TGA. Combinatorial samples of Li.Ni.O. cannot be made with x >?0.77 at 700?°C in air. In a flow of oxygen, 作者: 禮節(jié) 時間: 2025-3-28 06:32
Douglas C. Maynard,Daniel C. Feldman becomes more important and there is still sufficient thermal energy for atomic transport such that the R and M phases begin to appear in all samples. Further study is required to have a better understanding of the thermodynamics and kinetics of these phase transformations.作者: calamity 時間: 2025-3-28 11:50 作者: Generalize 時間: 2025-3-28 14:43 作者: 無可爭辯 時間: 2025-3-28 19:31 作者: 過份好問 時間: 2025-3-28 23:01 作者: Annotate 時間: 2025-3-29 07:00 作者: CAGE 時間: 2025-3-29 07:22
,Combinatorial Studies of the Spinel and Rocksalt Regions in the Li–Mn–Ni–O System,was used to determine the boundaries and showed excellent agreement with visually identified phases. Milligram-scale combinatorial samples can therefore be used to obtain a high degree of precision in the mapping of pseudo-ternary phase diagrams.作者: obstinate 時間: 2025-3-29 14:08 作者: 含沙射影 時間: 2025-3-29 16:01 作者: 遠足 時間: 2025-3-29 22:08
Axial Scattering from Thin Conessamples were cooled from 900?°C at a rate of 1?°C/min. These endpoints correspond to Co and Mn.Li domains with approximately 20?. disorder on the transition metal layers. Such disorder was also found over a range of temperatures during cooling using a Monte Carlo simulation.作者: Radiculopathy 時間: 2025-3-30 00:51
,Combinatorial Studies in the Li–Co–Mn–O System,samples were cooled from 900?°C at a rate of 1?°C/min. These endpoints correspond to Co and Mn.Li domains with approximately 20?. disorder on the transition metal layers. Such disorder was also found over a range of temperatures during cooling using a Monte Carlo simulation.